stainless steel bar 303

stainless steel bar 303

303 (UNS S30300) is a non-magnetic, austenitic, free-machining stainless steel that is a modification of the basic 10% chromium -8% nickel 
stainless steel specially designed to exhibit improved machinability while maintaining good mechanical and corrosion-resistant properties. 

Chemical Composition of 303 stainless steel 

C

Si

Mn

P

S

Cr

Ni

Mo

Max 0.15

Max 1.00

max 2.00

max 0.20

0.15-0.35

17.00-19.00

8.00-10.00

max 0.6

Mechanical Properties of 303 stainless steel bars

Yield Strength

0.2% (MPa) min

Tensile strength

(MPa) min

Elongation (% in 50mm) min

Rockwell B (HR B) max

Brinell (HB) max

450 - 650

750 - 800

34

95

262

303 stainless steel equivalent standard 

Euronorm

UNS

BS

En

Grade

1.4305

S30300

303S31

58M

303

303 stainless steel Corrosion Resistance
Alloy 303 is resistant to mildly corrosive environments. However, the alloy's corrosion resistance is inferior to 304 in most applications. 
Its corrosion resistance is superior to 416, another free-machining grade, but is somewhat inferior to other 400 series stainless steels which do not contain higher sulfur levels.
In order to obtain optimal corrosion resistance, it is recommended that Alloy 303 be chemically treated to remove sulfides from the final surfaces.

Heat Resistance of Stainless Steel Alloy 303
Grade 303 stainless steel has good resistance to oxidation when intermittently exposed to temperature up to 760°C temperatures. 
It also has good oxidation resistance in continuous service to 870°C. This, however, is not recommended as 303 is sensitive to carbide precipitation with continuous use at 425-860°C.

303 stainless steel bars Welding
Alloy 303 is not recommended for applications requiring welding. If it is necessary to weld the alloy, AWS E312 filler metal may be considered.

303 stainless steel Heat Treatment
Annealing – Heat to a minimum temperature of 1900oF (1038oC) and water quench or rapid cool by other means.
Hardening – Alloy 303 cannot be hardened by thermal treatment, it can only be hardened by cold working.

 Related Products:

stainless steel bar 201

stainless steel bar 301

stainless steel bar 303

stainless steel bar 303Cu

stainless steel bar 303F

stainless steel bar 304

stainless steel bar 304L

stainless steel bar 310S

stainless steel bar 316

stainless steel bar 316L

stainless steel bar SUS304

 
Copyright @2011 by Henan BEBON international co.,ltd. All rights reserved
Tel: 0086-371-86151827 86151627Fax: 0086-371-86011881E-mail: sales7@bebonchina.com