stainless steel bar 304L

stainless steel bar 304L

304L stainless steel application
Typical uses include architectural mouldings and trim, kitchen equipment,
welded components of chemical, textile,paper, pharmaceutical and chemical
industry processing equipment.

304L stainless steel is an extra low-carbon variation of Type 304 with a 0.03% maximum
carbon content that eliminates carbide precipitation due to welding. As a result,
this alloy can be used in the ”as-welded“ condition, even in severe corrosive conditions. It often eliminates the necessity of annealing weldments except for
applications specifying stress relief. It has slightly lower mechanical properties
than Type 304.

304L stainless steel bar mechanical properties

Hardness

Elongation
δ5
(%)

Area reduction
Ψ
(%)

Tensile Strength
σb
(MPa)

Yield Strength
σ0.2
(MPa)

Specific   Heat
C(20℃)
KJ/Kg.℃

Density
g·cm-3

HB

HRB

HV

 ≥40

≥50

≥520

≥205

0.502

7.93

≤187

≤90

≤200

304L material chemical composition

C

Cr

Ni

Mn

P

S

Si

other


0.03

18-20

9-13


2


0.035


0.03


1

-

304L stainless steel formability
304 and 304L have very good drawability. Their combination of low
yield strength and high elongation permits successful forming of complex
shapes. However, these grades work harden rapidly. To relieve stresses produced
 in severe forming or spinning,parts should be full annealed or stressrelief annealed as soon as possible after forming.

 Related Products:

stainless steel bar 201

stainless steel bar 301

stainless steel bar 303

stainless steel bar 303Cu

stainless steel bar 303F

stainless steel bar 304

stainless steel bar 304L

stainless steel bar 310S

stainless steel bar 316

stainless steel bar 316L

stainless steel bar SUS304

 
Copyright @2011 by Henan BEBON international co.,ltd. All rights reserved
Tel: 0086-371-86151827 86151627Fax: 0086-371-86011881E-mail: sales7@bebonchina.com