202 stainless steel coils

202 stainless steel coils

202 Stainless Steel is an austenitic chromium-nickel-manganese stainless steel which was developed to conserve nickel. 
202 is a lower cost alternative to conventional Cr-Ni stainless steels such as 301 and 304. Nickel is replaced by additions of manganese and nitrogen.

202 stainless steel coils application

202 stainless steel coils apply to cookware, hose clamps, piston rings, transit car structural member, transit car 
roofing/siding, thermal window spacers, air bag containers, and truck trailer posts and door frames.

202 stainless steel chemical composition 

Element

Content (%)

Iron, Fe

68

Chromium, Cr

17- 19

Manganese, Mn

7.50-10

Nickel, Ni

4-6

Silicon, Si

≤ 1

Nitrogen, N

≤ 0.25

Carbon, C

≤ 0.15

Phosphorous, P

≤ 0.060

Sulfur, S

≤ 0.030

202 stainless steel coils mechanical properties

Type

Yield Strength 0.2% 

offset (KSI)

Tensile Strength (KSI)

% Elongation
(2" Gauge length)

Hardness Rockwell

201 Ann

38 min.

75 min.

40% min.

HRB 95 max.

201 ¼ Hard

75 min.

125 min.

25.0 min.

25 – 32 HRC (typical)

201 ½ Hard

110 min.

150 min.

18.0 min.

32 - 37 HRC (typical)

201 ¾ Hard

135 min.

175 min.

12.0 min.

37 – 41 HRC (typical)

201 Full Hard

145 min.

185 min.

9.0 min.

41 – 46 HRC (typical)

202 Stainless steel coils specification 

Thickness Range: - 0.025mm – 4.00mm
Width: - Soft, Half Hard, Half Hard, ¾ Hard, Full Hard Spring Hard
Hardness: - Minimum 3.2mm to maximum 2000mm
Finish: - 2B, 2D, Bright Annealed, #3 Polish, #4 Polish and more

we are 202 stainless steel coils supplier, if you have any requires,contact us!

Copyright @2011 by Henan BEBON international co.,ltd. All rights reserved
Tel: 0086-371-86151827 86151627Fax: 0086-371-86011881E-mail: sales7@bebonchina.com